AWS E110C-K4 vs. AWS ER70S-A1
Both AWS E110C-K4 and AWS ER70S-A1 are iron alloys. They have a very high 97% of their average alloy composition in common.
For each property being compared, the top bar is AWS E110C-K4 and the bottom bar is AWS ER70S-A1.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 17 | |
| 22 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 850 | |
| 590 |
| Tensile Strength: Yield (Proof), MPa | 780 | |
| 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 41 | |
| 50 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 8.0 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 9.2 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.5 | |
| 2.5 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 1.5 |
| Embodied Energy, MJ/kg | 23 | |
| 20 |
| Embodied Water, L/kg | 54 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 1600 | |
| 540 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 30 | |
| 21 |
| Strength to Weight: Bending, points | 25 | |
| 20 |
| Thermal Diffusivity, mm2/s | 11 | |
| 14 |
| Thermal Shock Resistance, points | 25 | |
| 17 |
Alloy Composition
| Carbon (C), % | 0 to 0.15 | |
| 0 to 0.12 |
| Chromium (Cr), % | 0.15 to 0.65 | |
| 0 |
| Copper (Cu), % | 0 to 0.35 | |
| 0 to 0.35 |
| Iron (Fe), % | 92.1 to 98.4 | |
| 96.1 to 99.3 |
| Manganese (Mn), % | 0.75 to 2.3 | |
| 0 to 1.3 |
| Molybdenum (Mo), % | 0.25 to 0.65 | |
| 0.4 to 0.65 |
| Nickel (Ni), % | 0.5 to 2.5 | |
| 0 to 0.2 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.8 | |
| 0.3 to 0.7 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.025 |
| Vanadium (V), % | 0 to 0.030 | |
| 0 |
| Residuals, % | 0 | |
| 0 to 0.5 |