AWS E16-8-2 vs. AWS E309LMo
Both AWS E16-8-2 and AWS E309LMo are iron alloys. Both are furnished in the as-welded condition. They have 86% of their average alloy composition in common.
For each property being compared, the top bar is AWS E16-8-2 and the bottom bar is AWS E309LMo.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Elongation at Break, % | 40 | |
| 34 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 79 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 300 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1430 |
| Melting Onset (Solidus), °C | 1400 | |
| 1390 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 16 | |
| 15 |
| Thermal Expansion, µm/m-K | 14 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 2.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 2.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 22 |
| Density, g/cm3 | 7.9 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.2 | |
| 4.2 |
| Embodied Energy, MJ/kg | 45 | |
| 59 |
| Embodied Water, L/kg | 140 | |
| 180 |
Common Calculations
| PREN (Pitting Resistance) | 20 | |
| 32 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 22 | |
| 21 |
| Strength to Weight: Bending, points | 20 | |
| 20 |
| Thermal Diffusivity, mm2/s | 4.2 | |
| 3.9 |
| Thermal Shock Resistance, points | 16 | |
| 15 |
Alloy Composition
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.040 |
| Chromium (Cr), % | 14.5 to 16.5 | |
| 22 to 25 |
| Copper (Cu), % | 0 to 0.75 | |
| 0 to 0.75 |
| Iron (Fe), % | 68 to 76.5 | |
| 53.6 to 63.5 |
| Manganese (Mn), % | 0.5 to 2.5 | |
| 0.5 to 2.5 |
| Molybdenum (Mo), % | 1.0 to 2.0 | |
| 2.0 to 3.0 |
| Nickel (Ni), % | 7.5 to 9.5 | |
| 12 to 14 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |