AWS E209 vs. EN 1.7366 Steel
Both AWS E209 and EN 1.7366 steel are iron alloys. They have 64% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is AWS E209 and the bottom bar is EN 1.7366 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 17 | |
| 17 to 19 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 79 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 460 to 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 260 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1460 |
| Melting Onset (Solidus), °C | 1370 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Expansion, µm/m-K | 14 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 21 | |
| 4.3 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.4 | |
| 1.7 |
| Embodied Energy, MJ/kg | 63 | |
| 23 |
| Embodied Water, L/kg | 180 | |
| 69 |
Common Calculations
| PREN (Pitting Resistance) | 33 | |
| 6.8 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 28 | |
| 16 to 25 |
| Strength to Weight: Bending, points | 24 | |
| 17 to 23 |
| Thermal Shock Resistance, points | 19 | |
| 13 to 20 |
Alloy Composition
| Carbon (C), % | 0 to 0.060 | |
| 0 to 0.18 |
| Chromium (Cr), % | 20.5 to 24 | |
| 4.0 to 6.0 |
| Copper (Cu), % | 0 to 0.75 | |
| 0 |
| Iron (Fe), % | 51.5 to 64.3 | |
| 91.9 to 95.3 |
| Manganese (Mn), % | 4.0 to 7.0 | |
| 0.3 to 0.8 |
| Molybdenum (Mo), % | 1.5 to 3.0 | |
| 0.45 to 0.65 |
| Nickel (Ni), % | 9.5 to 12 | |
| 0 |
| Nitrogen (N), % | 0.1 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Vanadium (V), % | 0.1 to 0.3 | |
| 0 |