AWS E209 vs. EN 1.8151 Steel
Both AWS E209 and EN 1.8151 steel are iron alloys. They have 60% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is AWS E209 and the bottom bar is EN 1.8151 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 79 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 670 to 1940 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 270 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1440 |
| Melting Onset (Solidus), °C | 1370 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Expansion, µm/m-K | 14 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 21 | |
| 2.2 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 4.4 | |
| 1.8 |
| Embodied Energy, MJ/kg | 63 | |
| 25 |
| Embodied Water, L/kg | 180 | |
| 49 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 28 | |
| 24 to 70 |
| Strength to Weight: Bending, points | 24 | |
| 22 to 45 |
| Thermal Shock Resistance, points | 19 | |
| 20 to 58 |
Alloy Composition
| Carbon (C), % | 0 to 0.060 | |
| 0.4 to 0.5 |
| Chromium (Cr), % | 20.5 to 24 | |
| 0.4 to 0.8 |
| Copper (Cu), % | 0 to 0.75 | |
| 0 |
| Iron (Fe), % | 51.5 to 64.3 | |
| 95.9 to 97.2 |
| Manganese (Mn), % | 4.0 to 7.0 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 1.5 to 3.0 | |
| 0 |
| Nickel (Ni), % | 9.5 to 12 | |
| 0 |
| Nitrogen (N), % | 0.1 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 1.3 to 1.7 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |
| Vanadium (V), % | 0.1 to 0.3 | |
| 0.1 to 0.2 |