AWS E219 vs. ASTM A182 Grade F11 Class 2

Both AWS E219 and ASTM A182 grade F11 class 2 are iron alloys. They have 66% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS E219 and the bottom bar is ASTM A182 grade F11 class 2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 17
22
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 690
540

Thermal Properties

Latent Heat of Fusion, J/g 290
260
Melting Completion (Liquidus), °C 1400
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
39
Thermal Expansion, µm/m-K 15
13

Otherwise Unclassified Properties

Base Metal Price, % relative 15
2.9
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 3.1
1.6
Embodied Energy, MJ/kg 44
21
Embodied Water, L/kg 160
53

Common Calculations

PREN (Pitting Resistance) 25
3.0
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 25
19
Strength to Weight: Bending, points 23
19
Thermal Diffusivity, mm2/s 3.8
11
Thermal Shock Resistance, points 17
16

Alloy Composition

Carbon (C), % 0 to 0.060
0.1 to 0.2
Chromium (Cr), % 19 to 21.5
1.0 to 1.5
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 58.6 to 67.4
95.8 to 97.7
Manganese (Mn), % 8.0 to 10
0.3 to 0.8
Molybdenum (Mo), % 0 to 0.75
0.44 to 0.65
Nickel (Ni), % 5.5 to 7.0
0
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0.5 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.040