AWS E219 vs. Grade CW6M Nickel

AWS E219 belongs to the iron alloys classification, while grade CW6M nickel belongs to the nickel alloys. They have a modest 28% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS E219 and the bottom bar is grade CW6M nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
220
Elongation at Break, % 17
29
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
84
Tensile Strength: Ultimate (UTS), MPa 690
560

Thermal Properties

Latent Heat of Fusion, J/g 290
330
Melting Completion (Liquidus), °C 1400
1530
Melting Onset (Solidus), °C 1360
1470
Specific Heat Capacity, J/kg-K 480
430
Thermal Expansion, µm/m-K 15
12

Otherwise Unclassified Properties

Base Metal Price, % relative 15
65
Density, g/cm3 7.7
8.8
Embodied Carbon, kg CO2/kg material 3.1
13
Embodied Energy, MJ/kg 44
170
Embodied Water, L/kg 160
300

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 25
18
Strength to Weight: Bending, points 23
17
Thermal Shock Resistance, points 17
16

Alloy Composition

Carbon (C), % 0 to 0.060
0 to 0.070
Chromium (Cr), % 19 to 21.5
17 to 20
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 58.6 to 67.4
0 to 3.0
Manganese (Mn), % 8.0 to 10
0 to 1.0
Molybdenum (Mo), % 0 to 0.75
17 to 20
Nickel (Ni), % 5.5 to 7.0
54.9 to 66
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030