AWS E219 vs. Solder Alloy 102
AWS E219 belongs to the iron alloys classification, while solder alloy 102 belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is AWS E219 and the bottom bar is solder alloy 102.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
38 |
Elongation at Break, % | 17 | |
48 |
Poisson's Ratio | 0.28 | |
0.39 |
Shear Modulus, GPa | 78 | |
14 |
Tensile Strength: Ultimate (UTS), MPa | 690 | |
31 |
Thermal Properties
Latent Heat of Fusion, J/g | 290 | |
46 |
Melting Completion (Liquidus), °C | 1400 | |
180 |
Melting Onset (Solidus), °C | 1360 | |
180 |
Specific Heat Capacity, J/kg-K | 480 | |
190 |
Thermal Conductivity, W/m-K | 14 | |
53 |
Thermal Expansion, µm/m-K | 15 | |
25 |
Otherwise Unclassified Properties
Density, g/cm3 | 7.7 | |
8.8 |
Embodied Carbon, kg CO2/kg material | 3.1 | |
11 |
Embodied Energy, MJ/kg | 44 | |
180 |
Embodied Water, L/kg | 160 | |
930 |
Common Calculations
Stiffness to Weight: Axial, points | 14 | |
2.4 |
Stiffness to Weight: Bending, points | 25 | |
13 |
Strength to Weight: Axial, points | 25 | |
1.0 |
Strength to Weight: Bending, points | 23 | |
2.5 |
Thermal Diffusivity, mm2/s | 3.8 | |
32 |
Thermal Shock Resistance, points | 17 | |
2.4 |
Alloy Composition
Aluminum (Al), % | 0 | |
0 to 0.0010 |
Antimony (Sb), % | 0 | |
0 to 0.050 |
Arsenic (As), % | 0 | |
0 to 0.030 |
Bismuth (Bi), % | 0 | |
0 to 0.050 |
Cadmium (Cd), % | 0 | |
0 to 0.0020 |
Carbon (C), % | 0 to 0.060 | |
0 |
Chromium (Cr), % | 19 to 21.5 | |
0 |
Copper (Cu), % | 0 to 0.75 | |
0 to 0.080 |
Gold (Au), % | 0 | |
0 to 0.050 |
Indium (In), % | 0 | |
0 to 0.1 |
Iron (Fe), % | 58.6 to 67.4 | |
0 to 0.020 |
Lead (Pb), % | 0 | |
36 to 37.5 |
Manganese (Mn), % | 8.0 to 10 | |
0 |
Molybdenum (Mo), % | 0 to 0.75 | |
0 |
Nickel (Ni), % | 5.5 to 7.0 | |
0 to 0.010 |
Nitrogen (N), % | 0.1 to 0.3 | |
0 |
Phosphorus (P), % | 0 to 0.040 | |
0 |
Silicon (Si), % | 0 to 1.0 | |
0 |
Silver (Ag), % | 0 | |
0 to 0.1 |
Sulfur (S), % | 0 to 0.030 | |
0 |
Tin (Sn), % | 0 | |
62.5 to 63.5 |
Zinc (Zn), % | 0 | |
0 to 0.0010 |