AWS E219 vs. N10665 Nickel

AWS E219 belongs to the iron alloys classification, while N10665 nickel belongs to the nickel alloys. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS E219 and the bottom bar is N10665 nickel.

AWS E219 (W32310) Weld Metal UNS N10665 (2.4617, NiMo28) Nickel-Molybdenum Alloy

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		220

Elongation at Break, %		17
Elongation at Break, %		45

Poisson's Ratio		0.28
Poisson's Ratio		0.31

Shear Modulus, GPa		78
Shear Modulus, GPa		84

Tensile Strength: Ultimate (UTS), MPa		690
Tensile Strength: Ultimate (UTS), MPa		860

Thermal Properties

Latent Heat of Fusion, J/g		290
Latent Heat of Fusion, J/g		310

Melting Completion (Liquidus), °C		1400
Melting Completion (Liquidus), °C		1620

Melting Onset (Solidus), °C		1360
Melting Onset (Solidus), °C		1570

Specific Heat Capacity, J/kg-K		480
Specific Heat Capacity, J/kg-K		390

Thermal Conductivity, W/m-K		14
Thermal Conductivity, W/m-K		11

Thermal Expansion, µm/m-K		15
Thermal Expansion, µm/m-K		10

Otherwise Unclassified Properties

Base Metal Price, % relative		15
Base Metal Price, % relative		75

Density, g/cm³		7.7
Density, g/cm³		9.3

Embodied Carbon, kg CO₂/kg material		3.1
Embodied Carbon, kg CO₂/kg material		15

Embodied Energy, MJ/kg		44
Embodied Energy, MJ/kg		200

Embodied Water, L/kg		160
Embodied Water, L/kg		270

Common Calculations

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		22

Strength to Weight: Axial, points		25
Strength to Weight: Axial, points		26

Strength to Weight: Bending, points		23
Strength to Weight: Bending, points		22

Thermal Diffusivity, mm²/s		3.8
Thermal Diffusivity, mm²/s		3.1

Thermal Shock Resistance, points		17
Thermal Shock Resistance, points		27

Alloy Composition

Carbon (C), %		0 to 0.060
Carbon (C), %		0 to 0.020

Chromium (Cr), %		19 to 21.5
Chromium (Cr), %		0 to 1.0

Cobalt (Co), %		0
Cobalt (Co), %		0 to 1.0

Copper (Cu), %		0 to 0.75
Copper (Cu), %		0

Iron (Fe), %		58.6 to 67.4
Iron (Fe), %		0 to 2.0

Manganese (Mn), %		8.0 to 10
Manganese (Mn), %		0 to 1.0

Molybdenum (Mo), %		0 to 0.75
Molybdenum (Mo), %		26 to 30

Nickel (Ni), %		5.5 to 7.0
Nickel (Ni), %		64.8 to 74

Nitrogen (N), %		0.1 to 0.3
Nitrogen (N), %		0

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.040

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0 to 0.1

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030