AWS E219 vs. R31233 Cobalt
AWS E219 belongs to the iron alloys classification, while R31233 cobalt belongs to the cobalt alloys. They have a modest 31% of their average alloy composition in common, which, by itself, doesn't mean much. There are 21 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is AWS E219 and the bottom bar is R31233 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 220 |
| Elongation at Break, % | 17 | |
| 17 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 78 | |
| 85 |
| Tensile Strength: Ultimate (UTS), MPa | 690 | |
| 1020 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 320 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1350 |
| Melting Onset (Solidus), °C | 1360 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 440 |
| Thermal Conductivity, W/m-K | 14 | |
| 12 |
| Thermal Expansion, µm/m-K | 15 | |
| 13 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.7 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 3.1 | |
| 8.4 |
| Embodied Energy, MJ/kg | 44 | |
| 110 |
| Embodied Water, L/kg | 160 | |
| 480 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 25 | |
| 33 |
| Strength to Weight: Bending, points | 23 | |
| 26 |
| Thermal Diffusivity, mm2/s | 3.8 | |
| 3.2 |
| Thermal Shock Resistance, points | 17 | |
| 25 |
Alloy Composition
| Boron (B), % | 0 | |
| 0 to 0.015 |
| Carbon (C), % | 0 to 0.060 | |
| 0.020 to 0.1 |
| Chromium (Cr), % | 19 to 21.5 | |
| 23.5 to 27.5 |
| Cobalt (Co), % | 0 | |
| 44.7 to 63.3 |
| Copper (Cu), % | 0 to 0.75 | |
| 0 |
| Iron (Fe), % | 58.6 to 67.4 | |
| 1.0 to 5.0 |
| Manganese (Mn), % | 8.0 to 10 | |
| 0.1 to 1.5 |
| Molybdenum (Mo), % | 0 to 0.75 | |
| 4.0 to 6.0 |
| Nickel (Ni), % | 5.5 to 7.0 | |
| 7.0 to 11 |
| Nitrogen (N), % | 0.1 to 0.3 | |
| 0.030 to 0.12 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 1.0 | |
| 0.050 to 1.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.020 |
| Tungsten (W), % | 0 | |
| 1.0 to 3.0 |