AWS E2209 vs. EN 1.5418 Steel

Both AWS E2209 and EN 1.5418 steel are iron alloys. They have 64% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AWS E2209 and the bottom bar is EN 1.5418 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 770
490 to 1780

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
48
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 20
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.0
1.5
Embodied Energy, MJ/kg 55
19
Embodied Water, L/kg 170
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
17 to 63
Strength to Weight: Bending, points 24
18 to 42
Thermal Diffusivity, mm2/s 4.3
13
Thermal Shock Resistance, points 20
14 to 53

Alloy Composition

Carbon (C), % 0 to 0.040
0.35 to 0.4
Chromium (Cr), % 21.5 to 23.5
0
Copper (Cu), % 0 to 0.75
0 to 0.25
Iron (Fe), % 58.4 to 66.9
97.8 to 98.9
Manganese (Mn), % 0.5 to 2.0
0.6 to 0.9
Molybdenum (Mo), % 2.5 to 3.5
0.2 to 0.3
Nickel (Ni), % 8.5 to 10.5
0
Nitrogen (N), % 0.080 to 0.2
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.025