AWS E240 vs. EN 1.3551 Steel
Both AWS E240 and EN 1.3551 steel are iron alloys. They have 69% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is AWS E240 and the bottom bar is EN 1.3551 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 260 |
| Melting Completion (Liquidus), °C | 1390 | |
| 1490 |
| Melting Onset (Solidus), °C | 1350 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 460 |
| Thermal Conductivity, W/m-K | 15 | |
| 36 |
| Thermal Expansion, µm/m-K | 15 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 14 | |
| 9.0 |
| Density, g/cm3 | 7.7 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 4.9 |
| Embodied Energy, MJ/kg | 42 | |
| 71 |
| Embodied Water, L/kg | 160 | |
| 82 |
Common Calculations
| PREN (Pitting Resistance) | 22 | |
| 18 |
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 28 | |
| 26 |
| Strength to Weight: Bending, points | 24 | |
| 23 |
| Thermal Diffusivity, mm2/s | 3.9 | |
| 9.8 |
| Thermal Shock Resistance, points | 19 | |
| 21 |
Alloy Composition
| Carbon (C), % | 0 to 0.060 | |
| 0.77 to 0.85 |
| Chromium (Cr), % | 17 to 19 | |
| 3.9 to 4.3 |
| Copper (Cu), % | 0 to 0.75 | |
| 0 to 0.3 |
| Iron (Fe), % | 58.6 to 68.4 | |
| 88.8 to 91.1 |
| Manganese (Mn), % | 10.5 to 13.5 | |
| 0.15 to 0.35 |
| Molybdenum (Mo), % | 0 to 0.75 | |
| 4.0 to 4.5 |
| Nickel (Ni), % | 4.0 to 6.0 | |
| 0 |
| Nitrogen (N), % | 0.1 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |
| Tungsten (W), % | 0 | |
| 0 to 0.25 |
| Vanadium (V), % | 0 | |
| 0.9 to 1.1 |