AWS E240 vs. EN 1.4415 Stainless Steel

Both AWS E240 and EN 1.4415 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS E240 and the bottom bar is EN 1.4415 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 17
17 to 20
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
77
Tensile Strength: Ultimate (UTS), MPa 770
830 to 930

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Melting Completion (Liquidus), °C 1390
1460
Melting Onset (Solidus), °C 1350
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
19
Thermal Expansion, µm/m-K 15
9.9

Otherwise Unclassified Properties

Base Metal Price, % relative 14
13
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.0
3.6
Embodied Energy, MJ/kg 42
51
Embodied Water, L/kg 160
120

Common Calculations

PREN (Pitting Resistance) 22
19
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 28
29 to 33
Strength to Weight: Bending, points 24
25 to 27
Thermal Diffusivity, mm2/s 3.9
5.1
Thermal Shock Resistance, points 19
30 to 34

Alloy Composition

Carbon (C), % 0 to 0.060
0 to 0.030
Chromium (Cr), % 17 to 19
11.5 to 13.5
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 58.6 to 68.4
75.9 to 82.4
Manganese (Mn), % 10.5 to 13.5
0 to 0.5
Molybdenum (Mo), % 0 to 0.75
1.5 to 2.5
Nickel (Ni), % 4.0 to 6.0
4.5 to 6.5
Nitrogen (N), % 0.1 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0 to 0.010
Vanadium (V), % 0
0.1 to 0.5