AWS E240 vs. N07750 Nickel
AWS E240 belongs to the iron alloys classification, while N07750 nickel belongs to the nickel alloys. They have a modest 29% of their average alloy composition in common, which, by itself, doesn't mean much. There are 22 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is AWS E240 and the bottom bar is N07750 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 17 | |
| 25 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 1200 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 310 |
| Melting Completion (Liquidus), °C | 1390 | |
| 1430 |
| Melting Onset (Solidus), °C | 1350 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 460 |
| Thermal Conductivity, W/m-K | 15 | |
| 13 |
| Thermal Expansion, µm/m-K | 15 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 14 | |
| 60 |
| Density, g/cm3 | 7.7 | |
| 8.4 |
| Embodied Carbon, kg CO2/kg material | 3.0 | |
| 10 |
| Embodied Energy, MJ/kg | 42 | |
| 150 |
| Embodied Water, L/kg | 160 | |
| 260 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 28 | |
| 40 |
| Strength to Weight: Bending, points | 24 | |
| 30 |
| Thermal Diffusivity, mm2/s | 3.9 | |
| 3.3 |
| Thermal Shock Resistance, points | 19 | |
| 36 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.4 to 1.0 |
| Carbon (C), % | 0 to 0.060 | |
| 0 to 0.080 |
| Chromium (Cr), % | 17 to 19 | |
| 14 to 17 |
| Cobalt (Co), % | 0 | |
| 0 to 1.0 |
| Copper (Cu), % | 0 to 0.75 | |
| 0 to 0.5 |
| Iron (Fe), % | 58.6 to 68.4 | |
| 5.0 to 9.0 |
| Manganese (Mn), % | 10.5 to 13.5 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 to 0.75 | |
| 0 |
| Nickel (Ni), % | 4.0 to 6.0 | |
| 70 to 77.7 |
| Niobium (Nb), % | 0 | |
| 0.7 to 1.2 |
| Nitrogen (N), % | 0.1 to 0.3 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 2.3 to 2.8 |