AWS E2553 vs. C27000 Brass

AWS E2553 belongs to the iron alloys classification, while C27000 brass belongs to the copper alloys. There are 23 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS E2553 and the bottom bar is C27000 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Poisson's Ratio 0.27
0.31
Shear Modulus, GPa 80
40
Tensile Strength: Ultimate (UTS), MPa 850
370 to 650

Thermal Properties

Latent Heat of Fusion, J/g 300
180
Melting Completion (Liquidus), °C 1440
930
Melting Onset (Solidus), °C 1390
900
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 16
120
Thermal Expansion, µm/m-K 14
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
27
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
30

Otherwise Unclassified Properties

Base Metal Price, % relative 21
24
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 4.0
2.7
Embodied Energy, MJ/kg 56
45
Embodied Water, L/kg 190
320

Common Calculations

Stiffness to Weight: Axial, points 14
7.2
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 30
13 to 22
Strength to Weight: Bending, points 26
14 to 21
Thermal Diffusivity, mm2/s 4.3
37
Thermal Shock Resistance, points 21
12 to 22

Alloy Composition

Carbon (C), % 0 to 0.060
0
Chromium (Cr), % 24 to 27
0
Copper (Cu), % 1.5 to 2.5
63 to 68.5
Iron (Fe), % 55.2 to 64.5
0 to 0.1
Lead (Pb), % 0
0 to 0.070
Manganese (Mn), % 0.5 to 1.5
0
Molybdenum (Mo), % 2.9 to 3.9
0
Nickel (Ni), % 6.5 to 8.5
0
Nitrogen (N), % 0.1 to 0.25
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0
Zinc (Zn), % 0
31 to 37
Residuals, % 0
0 to 0.3