AWS E2594 vs. S66286 Stainless Steel

Both AWS E2594 and S66286 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E2594 and the bottom bar is S66286 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 17
17 to 40
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
75
Tensile Strength: Ultimate (UTS), MPa 850
620 to 1020

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1400
1370
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
15
Thermal Expansion, µm/m-K 14
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.2

Otherwise Unclassified Properties

Base Metal Price, % relative 22
26
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 4.3
6.0
Embodied Energy, MJ/kg 60
87
Embodied Water, L/kg 190
170

Common Calculations

PREN (Pitting Resistance) 43
19
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 30
22 to 36
Strength to Weight: Bending, points 25
20 to 28
Thermal Diffusivity, mm2/s 4.3
4.0
Thermal Shock Resistance, points 21
13 to 22

Alloy Composition

Aluminum (Al), % 0
0 to 0.35
Boron (B), % 0
0.0010 to 0.010
Carbon (C), % 0 to 0.040
0 to 0.080
Chromium (Cr), % 24 to 27
13.5 to 16
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 53.8 to 63.8
49.1 to 59.5
Manganese (Mn), % 0.5 to 2.0
0 to 2.0
Molybdenum (Mo), % 3.5 to 4.5
1.0 to 1.5
Nickel (Ni), % 8.0 to 10.5
24 to 27
Nitrogen (N), % 0.2 to 0.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030
Titanium (Ti), % 0
1.9 to 2.4
Vanadium (V), % 0
0.1 to 0.5