AWS E307 vs. EN 1.4852 Stainless Steel

Both AWS E307 and EN 1.4852 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E307 and the bottom bar is EN 1.4852 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
4.6
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
77
Tensile Strength: Ultimate (UTS), MPa 660
490

Thermal Properties

Latent Heat of Fusion, J/g 290
330
Melting Completion (Liquidus), °C 1420
1380
Melting Onset (Solidus), °C 1370
1340
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
13
Thermal Expansion, µm/m-K 14
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 17
41
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 3.5
6.9
Embodied Energy, MJ/kg 49
100
Embodied Water, L/kg 160
220

Common Calculations

PREN (Pitting Resistance) 23
26
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24
17
Strength to Weight: Bending, points 22
18
Thermal Diffusivity, mm2/s 4.1
3.4
Thermal Shock Resistance, points 17
11

Alloy Composition

Carbon (C), % 0.040 to 0.14
0.3 to 0.5
Chromium (Cr), % 18 to 21.5
24 to 27
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 59.6 to 69.2
29.6 to 40.9
Manganese (Mn), % 3.3 to 4.8
0 to 2.0
Molybdenum (Mo), % 0.5 to 1.5
0 to 0.5
Nickel (Ni), % 9.0 to 10.7
33 to 36
Niobium (Nb), % 0
0.8 to 1.8
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
1.0 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.030