AWS E307 vs. SAE-AISI 1536 Steel

Both AWS E307 and SAE-AISI 1536 steel are iron alloys. They have 66% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E307 and the bottom bar is SAE-AISI 1536 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
14 to 18
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 660
640 to 720

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 14
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 17
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.5
1.4
Embodied Energy, MJ/kg 49
19
Embodied Water, L/kg 160
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24
23 to 25
Strength to Weight: Bending, points 22
21 to 23
Thermal Diffusivity, mm2/s 4.1
14
Thermal Shock Resistance, points 17
20 to 23

Alloy Composition

Carbon (C), % 0.040 to 0.14
0.3 to 0.37
Chromium (Cr), % 18 to 21.5
0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 59.6 to 69.2
98 to 98.5
Manganese (Mn), % 3.3 to 4.8
1.2 to 1.5
Molybdenum (Mo), % 0.5 to 1.5
0
Nickel (Ni), % 9.0 to 10.7
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0 to 0.050