AWS E308L vs. CC755S Brass

AWS E308L belongs to the iron alloys classification, while CC755S brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS E308L and the bottom bar is CC755S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
100
Elongation at Break, % 40
9.5
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 78
40
Tensile Strength: Ultimate (UTS), MPa 580
390

Thermal Properties

Latent Heat of Fusion, J/g 290
170
Melting Completion (Liquidus), °C 1420
820
Melting Onset (Solidus), °C 1380
780
Specific Heat Capacity, J/kg-K 480
390
Thermal Conductivity, W/m-K 16
120
Thermal Expansion, µm/m-K 14
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
27
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
30

Otherwise Unclassified Properties

Base Metal Price, % relative 16
23
Density, g/cm3 7.8
8.1
Embodied Carbon, kg CO2/kg material 3.2
2.7
Embodied Energy, MJ/kg 46
46
Embodied Water, L/kg 150
330

Common Calculations

Stiffness to Weight: Axial, points 14
7.1
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 21
14
Strength to Weight: Bending, points 20
15
Thermal Diffusivity, mm2/s 4.1
38
Thermal Shock Resistance, points 15
13

Alloy Composition

Aluminum (Al), % 0
0.4 to 0.7
Carbon (C), % 0 to 0.040
0
Chromium (Cr), % 18 to 21
0
Copper (Cu), % 0 to 0.75
59.5 to 61
Iron (Fe), % 62.9 to 72.5
0.050 to 0.2
Lead (Pb), % 0
1.2 to 1.7
Manganese (Mn), % 0.5 to 2.5
0 to 0.050
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 9.0 to 11
0 to 0.2
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0 to 0.050
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 0.3
Zinc (Zn), % 0
35.8 to 38.9