AWS E308LMo vs. AWS ERNiCrMo-3
AWS E308LMo belongs to the iron alloys classification, while AWS ERNiCrMo-3 belongs to the nickel alloys. They have a modest 36% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is AWS E308LMo and the bottom bar is AWS ERNiCrMo-3.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 200 | |
200 |
Elongation at Break, % | 40 | |
34 |
Poisson's Ratio | 0.28 | |
0.29 |
Shear Modulus, GPa | 78 | |
79 |
Tensile Strength: Ultimate (UTS), MPa | 580 | |
870 |
Thermal Properties
Latent Heat of Fusion, J/g | 290 | |
330 |
Melting Completion (Liquidus), °C | 1440 | |
1480 |
Melting Onset (Solidus), °C | 1400 | |
1430 |
Specific Heat Capacity, J/kg-K | 470 | |
440 |
Thermal Conductivity, W/m-K | 16 | |
11 |
Thermal Expansion, µm/m-K | 14 | |
12 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.0 | |
1.3 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.3 | |
1.4 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 19 | |
80 |
Density, g/cm3 | 7.9 | |
8.6 |
Embodied Carbon, kg CO2/kg material | 3.8 | |
14 |
Embodied Energy, MJ/kg | 53 | |
190 |
Embodied Water, L/kg | 160 | |
290 |
Common Calculations
Stiffness to Weight: Axial, points | 14 | |
13 |
Stiffness to Weight: Bending, points | 25 | |
23 |
Strength to Weight: Axial, points | 21 | |
28 |
Strength to Weight: Bending, points | 20 | |
24 |
Thermal Diffusivity, mm2/s | 4.2 | |
2.8 |
Thermal Shock Resistance, points | 15 | |
25 |
Alloy Composition
Aluminum (Al), % | 0 | |
0 to 0.4 |
Carbon (C), % | 0 to 0.040 | |
0 to 0.010 |
Chromium (Cr), % | 18 to 21 | |
20 to 23 |
Copper (Cu), % | 0 to 0.75 | |
0 to 0.5 |
Iron (Fe), % | 59.6 to 70.5 | |
0 to 5.0 |
Manganese (Mn), % | 0.5 to 2.5 | |
0 to 0.5 |
Molybdenum (Mo), % | 2.0 to 3.0 | |
8.0 to 10 |
Nickel (Ni), % | 9.0 to 12 | |
58 to 68.9 |
Niobium (Nb), % | 0 | |
3.2 to 4.2 |
Phosphorus (P), % | 0 to 0.040 | |
0 to 0.020 |
Silicon (Si), % | 0 to 1.0 | |
0 to 0.5 |
Sulfur (S), % | 0 to 0.030 | |
0 to 0.015 |
Titanium (Ti), % | 0 | |
0 to 0.4 |
Residuals, % | 0 | |
0 to 0.5 |