AWS E308LMo vs. EN 1.4515 Stainless Steel

Both AWS E308LMo and EN 1.4515 stainless steel are iron alloys. They have a moderately high 93% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E308LMo and the bottom bar is EN 1.4515 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 40
25
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 78
80
Tensile Strength: Ultimate (UTS), MPa 580
730

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 16
16
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 19
19
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.8
3.8
Embodied Energy, MJ/kg 53
53
Embodied Water, L/kg 160
180

Common Calculations

PREN (Pitting Resistance) 28
38
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
26
Strength to Weight: Bending, points 20
23
Thermal Diffusivity, mm2/s 4.2
4.3
Thermal Shock Resistance, points 15
20

Alloy Composition

Carbon (C), % 0 to 0.040
0 to 0.030
Chromium (Cr), % 18 to 21
24.5 to 26.5
Copper (Cu), % 0 to 0.75
0.8 to 1.3
Iron (Fe), % 59.6 to 70.5
58.4 to 66.6
Manganese (Mn), % 0.5 to 2.5
0 to 2.0
Molybdenum (Mo), % 2.0 to 3.0
2.5 to 3.5
Nickel (Ni), % 9.0 to 12
5.5 to 7.0
Nitrogen (N), % 0
0.12 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.020