MakeItFrom.com
Menu (ESC)

AWS E308Mo vs. EN 1.4807 Stainless Steel

Both AWS E308Mo and EN 1.4807 stainless steel are iron alloys. They have 72% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E308Mo and the bottom bar is EN 1.4807 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 40
4.5
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
75
Tensile Strength: Ultimate (UTS), MPa 620
480

Thermal Properties

Latent Heat of Fusion, J/g 290
320
Melting Completion (Liquidus), °C 1440
1390
Melting Onset (Solidus), °C 1400
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 16
12
Thermal Expansion, µm/m-K 14
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 19
39
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 3.8
6.8
Embodied Energy, MJ/kg 53
97
Embodied Water, L/kg 160
190

Common Calculations

PREN (Pitting Resistance) 28
19
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
17
Strength to Weight: Bending, points 20
17
Thermal Diffusivity, mm2/s 4.2
3.2
Thermal Shock Resistance, points 16
12

Alloy Composition

Carbon (C), % 0 to 0.080
0.3 to 0.5
Chromium (Cr), % 18 to 21
17 to 20
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 59.6 to 70.5
36.6 to 46.7
Manganese (Mn), % 0.5 to 2.5
0 to 2.0
Molybdenum (Mo), % 2.0 to 3.0
0 to 0.5
Nickel (Ni), % 9.0 to 12
34 to 36
Niobium (Nb), % 0
1.0 to 1.8
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
1.0 to 2.5
Sulfur (S), % 0 to 0.030
0 to 0.030