AWS E309L vs. SAE-AISI 52100 Steel

Both AWS E309L and SAE-AISI 52100 steel are iron alloys. They have 63% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS E309L and the bottom bar is SAE-AISI 52100 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
10 to 20
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 79
72
Tensile Strength: Ultimate (UTS), MPa 580
590 to 2010

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
47
Thermal Expansion, µm/m-K 14
12 to 13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 20
2.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.7
1.5
Embodied Energy, MJ/kg 52
20
Embodied Water, L/kg 180
51

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
21 to 72
Strength to Weight: Bending, points 20
20 to 45
Thermal Diffusivity, mm2/s 4.0
13
Thermal Shock Resistance, points 15
19 to 61

Alloy Composition

Carbon (C), % 0 to 0.040
0.93 to 1.1
Chromium (Cr), % 22 to 25
1.4 to 1.6
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 55.9 to 65.5
96.5 to 97.3
Manganese (Mn), % 0.5 to 2.5
0.25 to 0.45
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 12 to 14
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.015