AWS E309LMo vs. EN 1.4460 Stainless Steel

Both AWS E309LMo and EN 1.4460 stainless steel are iron alloys. They have a moderately high 91% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E309LMo and the bottom bar is EN 1.4460 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
21
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 79
80
Tensile Strength: Ultimate (UTS), MPa 580
750

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Melting Completion (Liquidus), °C 1430
1430
Melting Onset (Solidus), °C 1390
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 22
18
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.2
3.4
Embodied Energy, MJ/kg 59
48
Embodied Water, L/kg 180
180

Common Calculations

PREN (Pitting Resistance) 32
34
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 21
27
Strength to Weight: Bending, points 20
24
Thermal Diffusivity, mm2/s 3.9
4.0
Thermal Shock Resistance, points 15
20

Alloy Composition

Carbon (C), % 0 to 0.040
0 to 0.050
Chromium (Cr), % 22 to 25
25 to 28
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 53.6 to 63.5
60.2 to 69.2
Manganese (Mn), % 0.5 to 2.5
0 to 2.0
Molybdenum (Mo), % 2.0 to 3.0
1.3 to 2.0
Nickel (Ni), % 12 to 14
4.5 to 6.5
Nitrogen (N), % 0
0.050 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015