AWS E309Mo vs. EN 1.4409 Stainless Steel

Both AWS E309Mo and EN 1.4409 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS E309Mo and the bottom bar is EN 1.4409 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
34
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
78
Tensile Strength: Ultimate (UTS), MPa 620
490

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Melting Completion (Liquidus), °C 1430
1440
Melting Onset (Solidus), °C 1390
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 14
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 22
19
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.2
3.7
Embodied Energy, MJ/kg 59
52
Embodied Water, L/kg 180
160

Common Calculations

PREN (Pitting Resistance) 32
28
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
17
Strength to Weight: Bending, points 20
18
Thermal Diffusivity, mm2/s 3.9
4.1
Thermal Shock Resistance, points 15
11

Alloy Composition

Carbon (C), % 0 to 0.12
0 to 0.030
Chromium (Cr), % 22 to 25
18 to 20
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 53.6 to 63.5
61.7 to 71
Manganese (Mn), % 0.5 to 2.5
0 to 2.0
Molybdenum (Mo), % 2.0 to 3.0
2.0 to 2.5
Nickel (Ni), % 12 to 14
9.0 to 12
Nitrogen (N), % 0
0 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.025