AWS E309Mo vs. EN 1.4658 Stainless Steel

Both AWS E309Mo and EN 1.4658 stainless steel are iron alloys. They have a moderately high 92% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS E309Mo and the bottom bar is EN 1.4658 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 34
28
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 79
81
Tensile Strength: Ultimate (UTS), MPa 620
900

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
16
Thermal Expansion, µm/m-K 14
13

Otherwise Unclassified Properties

Base Metal Price, % relative 22
25
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.2
4.5
Embodied Energy, MJ/kg 59
61
Embodied Water, L/kg 180
200

Common Calculations

PREN (Pitting Resistance) 32
49
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
32
Strength to Weight: Bending, points 20
26
Thermal Diffusivity, mm2/s 3.9
4.3
Thermal Shock Resistance, points 15
24

Alloy Composition

Carbon (C), % 0 to 0.12
0 to 0.030
Chromium (Cr), % 22 to 25
26 to 29
Cobalt (Co), % 0
0.5 to 2.0
Copper (Cu), % 0 to 0.75
0 to 1.0
Iron (Fe), % 53.6 to 63.5
50.9 to 63.7
Manganese (Mn), % 0.5 to 2.5
0 to 1.5
Molybdenum (Mo), % 2.0 to 3.0
4.0 to 5.0
Nickel (Ni), % 12 to 14
5.5 to 9.5
Nitrogen (N), % 0
0.3 to 0.5
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.5
Sulfur (S), % 0 to 0.030
0 to 0.010