AWS E309Mo vs. SAE-AISI 1345 Steel

Both AWS E309Mo and SAE-AISI 1345 steel are iron alloys. They have 60% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS E309Mo and the bottom bar is SAE-AISI 1345 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
11 to 23
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
72
Tensile Strength: Ultimate (UTS), MPa 620
590 to 730

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Melting Completion (Liquidus), °C 1430
1450
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 14
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 22
1.9
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.2
1.4
Embodied Energy, MJ/kg 59
19
Embodied Water, L/kg 180
48

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
21 to 26
Strength to Weight: Bending, points 20
20 to 23
Thermal Diffusivity, mm2/s 3.9
14
Thermal Shock Resistance, points 15
19 to 23

Alloy Composition

Carbon (C), % 0 to 0.12
0.43 to 0.48
Chromium (Cr), % 22 to 25
0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 53.6 to 63.5
97.2 to 97.8
Manganese (Mn), % 0.5 to 2.5
1.6 to 1.9
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 12 to 14
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.040