AWS E310 vs. EN 1.4435 Stainless Steel

Both AWS E310 and EN 1.4435 stainless steel are iron alloys. They have 83% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E310 and the bottom bar is EN 1.4435 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
43
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
78
Tensile Strength: Ultimate (UTS), MPa 620
610

Thermal Properties

Latent Heat of Fusion, J/g 300
290
Melting Completion (Liquidus), °C 1400
1440
Melting Onset (Solidus), °C 1360
1400
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 14
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 26
21
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.6
4.1
Embodied Energy, MJ/kg 65
57
Embodied Water, L/kg 200
160

Common Calculations

PREN (Pitting Resistance) 28
28
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
21
Strength to Weight: Bending, points 20
20
Thermal Diffusivity, mm2/s 3.7
4.0
Thermal Shock Resistance, points 15
14

Alloy Composition

Carbon (C), % 0.080 to 0.2
0 to 0.030
Chromium (Cr), % 25 to 28
17 to 19
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 44.5 to 53.9
59.8 to 68
Manganese (Mn), % 1.0 to 2.5
0 to 2.0
Molybdenum (Mo), % 0 to 0.75
2.5 to 3.0
Nickel (Ni), % 20 to 22.5
12.5 to 15
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015