AWS E310 vs. C84100 Brass

AWS E310 belongs to the iron alloys classification, while C84100 brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS E310 and the bottom bar is C84100 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34
13
Poisson's Ratio 0.27
0.33
Shear Modulus, GPa 79
39
Tensile Strength: Ultimate (UTS), MPa 620
230

Thermal Properties

Latent Heat of Fusion, J/g 300
190
Melting Completion (Liquidus), °C 1400
1000
Melting Onset (Solidus), °C 1360
810
Specific Heat Capacity, J/kg-K 480
380
Thermal Conductivity, W/m-K 14
110
Thermal Expansion, µm/m-K 14
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
23
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
25

Otherwise Unclassified Properties

Base Metal Price, % relative 26
29
Density, g/cm3 7.9
8.5
Embodied Carbon, kg CO2/kg material 4.6
2.9
Embodied Energy, MJ/kg 65
48
Embodied Water, L/kg 200
340

Common Calculations

Stiffness to Weight: Axial, points 14
7.1
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 22
7.4
Strength to Weight: Bending, points 20
9.7
Thermal Diffusivity, mm2/s 3.7
33
Thermal Shock Resistance, points 15
7.8

Alloy Composition

Aluminum (Al), % 0
0 to 0.010
Antimony (Sb), % 0
0 to 0.050
Bismuth (Bi), % 0
0 to 0.090
Carbon (C), % 0.080 to 0.2
0
Chromium (Cr), % 25 to 28
0
Copper (Cu), % 0 to 0.75
78 to 85
Iron (Fe), % 44.5 to 53.9
0 to 0.3
Lead (Pb), % 0
0.050 to 0.25
Manganese (Mn), % 1.0 to 2.5
0
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 20 to 22.5
0 to 0.5
Phosphorus (P), % 0 to 0.030
0 to 0.050
Silicon (Si), % 0 to 0.75
0 to 0.010
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
1.5 to 4.5
Zinc (Zn), % 0
12 to 20
Residuals, % 0
0 to 0.5