AWS E310 vs. C91300 Bell Metal

AWS E310 belongs to the iron alloys classification, while C91300 bell metal belongs to the copper alloys. There are 22 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS E310 and the bottom bar is C91300 bell metal.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
100
Elongation at Break, % 34
0.5
Poisson's Ratio 0.27
0.34
Shear Modulus, GPa 79
38
Tensile Strength: Ultimate (UTS), MPa 620
240

Thermal Properties

Latent Heat of Fusion, J/g 300
180
Melting Completion (Liquidus), °C 1400
890
Melting Onset (Solidus), °C 1360
820
Specific Heat Capacity, J/kg-K 480
360
Thermal Expansion, µm/m-K 14
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
7.4

Otherwise Unclassified Properties

Base Metal Price, % relative 26
39
Density, g/cm3 7.9
8.6
Embodied Carbon, kg CO2/kg material 4.6
4.5
Embodied Energy, MJ/kg 65
74
Embodied Water, L/kg 200
460

Common Calculations

Stiffness to Weight: Axial, points 14
6.6
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 22
7.8
Strength to Weight: Bending, points 20
10
Thermal Shock Resistance, points 15
9.3

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.2
Carbon (C), % 0.080 to 0.2
0
Chromium (Cr), % 25 to 28
0
Copper (Cu), % 0 to 0.75
79 to 82
Iron (Fe), % 44.5 to 53.9
0 to 0.25
Lead (Pb), % 0
0 to 0.25
Manganese (Mn), % 1.0 to 2.5
0
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 20 to 22.5
0 to 0.5
Phosphorus (P), % 0 to 0.030
0 to 1.5
Silicon (Si), % 0 to 0.75
0 to 0.0050
Sulfur (S), % 0 to 0.030
0 to 0.050
Tin (Sn), % 0
18 to 20
Zinc (Zn), % 0
0 to 0.25
Residuals, % 0
0 to 0.6