AWS E310H vs. AISI 201 Stainless Steel

Both AWS E310H and AISI 201 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS E310H and the bottom bar is AISI 201 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 11
4.6 to 51
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 79
77
Tensile Strength: Ultimate (UTS), MPa 690
650 to 1450

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Melting Completion (Liquidus), °C 1400
1410
Melting Onset (Solidus), °C 1350
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 14
15
Thermal Expansion, µm/m-K 14
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.9

Otherwise Unclassified Properties

Base Metal Price, % relative 26
12
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.6
2.6
Embodied Energy, MJ/kg 65
38
Embodied Water, L/kg 200
140

Common Calculations

PREN (Pitting Resistance) 28
19
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 25
23 to 52
Strength to Weight: Bending, points 22
22 to 37
Thermal Diffusivity, mm2/s 3.8
4.0
Thermal Shock Resistance, points 17
14 to 32

Alloy Composition

Carbon (C), % 0.35 to 0.45
0 to 0.15
Chromium (Cr), % 25 to 28
16 to 18
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 44.2 to 53.7
67.5 to 75
Manganese (Mn), % 1.0 to 2.5
5.5 to 7.5
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 20 to 22.5
3.5 to 5.5
Nitrogen (N), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.030
0 to 0.060
Silicon (Si), % 0 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030