AWS E310H vs. Grade 250 Maraging Steel
Both AWS E310H and grade 250 maraging steel are iron alloys. They have 67% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AWS E310H and the bottom bar is grade 250 maraging steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 11 | |
| 7.3 to 17 |
| Poisson's Ratio | 0.27 | |
| 0.3 |
| Shear Modulus, GPa | 79 | |
| 75 |
| Tensile Strength: Ultimate (UTS), MPa | 690 | |
| 970 to 1800 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 270 |
| Melting Completion (Liquidus), °C | 1400 | |
| 1480 |
| Melting Onset (Solidus), °C | 1350 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 450 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 26 | |
| 32 |
| Density, g/cm3 | 7.9 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 4.6 | |
| 4.9 |
| Embodied Energy, MJ/kg | 65 | |
| 65 |
| Embodied Water, L/kg | 200 | |
| 140 |
Common Calculations
| PREN (Pitting Resistance) | 28 | |
| 16 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 25 | |
| 33 to 61 |
| Strength to Weight: Bending, points | 22 | |
| 26 to 40 |
| Thermal Shock Resistance, points | 17 | |
| 29 to 54 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.050 to 0.15 |
| Boron (B), % | 0 | |
| 0 to 0.0030 |
| Calcium (Ca), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0.35 to 0.45 | |
| 0 to 0.030 |
| Chromium (Cr), % | 25 to 28 | |
| 0 |
| Cobalt (Co), % | 0 | |
| 7.0 to 8.5 |
| Copper (Cu), % | 0 to 0.75 | |
| 0 |
| Iron (Fe), % | 44.2 to 53.7 | |
| 66.3 to 71.1 |
| Manganese (Mn), % | 1.0 to 2.5 | |
| 0 to 0.1 |
| Molybdenum (Mo), % | 0 to 0.75 | |
| 4.6 to 5.2 |
| Nickel (Ni), % | 20 to 22.5 | |
| 17 to 19 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.010 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |
| Titanium (Ti), % | 0 | |
| 0.3 to 0.5 |
| Zirconium (Zr), % | 0 | |
| 0 to 0.020 |