AWS E310Mo vs. EN 2.4608 Nickel

AWS E310Mo belongs to the iron alloys classification, while EN 2.4608 nickel belongs to the nickel alloys. They have 68% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E310Mo and the bottom bar is EN 2.4608 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 34
34
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
81
Tensile Strength: Ultimate (UTS), MPa 620
620

Thermal Properties

Latent Heat of Fusion, J/g 310
330
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 14
11
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 28
55
Density, g/cm3 7.9
8.5
Embodied Carbon, kg CO2/kg material 5.1
8.4
Embodied Energy, MJ/kg 71
120
Embodied Water, L/kg 210
270

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 22
20
Strength to Weight: Bending, points 20
19
Thermal Diffusivity, mm2/s 3.7
2.9
Thermal Shock Resistance, points 15
16

Alloy Composition

Carbon (C), % 0 to 0.12
0.030 to 0.080
Chromium (Cr), % 25 to 28
24 to 26
Cobalt (Co), % 0
2.5 to 4.0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 42.8 to 52
11.4 to 23.8
Manganese (Mn), % 1.0 to 2.5
0 to 2.0
Molybdenum (Mo), % 2.0 to 3.0
2.5 to 4.0
Nickel (Ni), % 20 to 22
44 to 47
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.75
0.7 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.015
Tungsten (W), % 0
2.5 to 4.0