AWS E312 vs. SAE-AISI P3 Steel

Both AWS E312 and SAE-AISI P3 steel are iron alloys. They have 61% of their average alloy composition in common. There are 19 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS E312 and the bottom bar is SAE-AISI P3 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 740
410 to 1980

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Melting Completion (Liquidus), °C 1410
1460
Melting Onset (Solidus), °C 1360
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 15
12

Otherwise Unclassified Properties

Base Metal Price, % relative 20
2.8
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 3.6
1.5
Embodied Energy, MJ/kg 52
20
Embodied Water, L/kg 200
50

Common Calculations

Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 27
15 to 70
Strength to Weight: Bending, points 24
16 to 44
Thermal Shock Resistance, points 18
14 to 65

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.1
Chromium (Cr), % 28 to 32
0.4 to 0.75
Copper (Cu), % 0 to 0.75
0 to 0.25
Iron (Fe), % 52.3 to 63.5
96.3 to 98.4
Manganese (Mn), % 0.5 to 2.5
0.2 to 0.6
Molybdenum (Mo), % 0 to 0.75
0
Nickel (Ni), % 8.0 to 10.5
1.0 to 1.5
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.030