AWS E3155 vs. EN 1.6570 Steel

Both AWS E3155 and EN 1.6570 steel are iron alloys. They have a modest 34% of their average alloy composition in common, which, by itself, doesn't mean much. There are 23 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E3155 and the bottom bar is EN 1.6570 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 23
11 to 17
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 81
73
Tensile Strength: Ultimate (UTS), MPa 770
910 to 1130

Thermal Properties

Latent Heat of Fusion, J/g 310
250
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
40
Thermal Expansion, µm/m-K 13
13

Otherwise Unclassified Properties

Base Metal Price, % relative 70
3.9
Density, g/cm3 8.4
7.9
Embodied Carbon, kg CO2/kg material 7.7
1.7
Embodied Energy, MJ/kg 110
23
Embodied Water, L/kg 300
56

Common Calculations

PREN (Pitting Resistance) 35
2.5
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 26
32 to 40
Strength to Weight: Bending, points 22
27 to 31
Thermal Diffusivity, mm2/s 3.3
11
Thermal Shock Resistance, points 20
27 to 33

Alloy Composition

Carbon (C), % 0 to 0.1
0.28 to 0.35
Chromium (Cr), % 20 to 22.5
1.0 to 1.4
Cobalt (Co), % 18.5 to 21
0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 23.3 to 36.3
94 to 96.2
Manganese (Mn), % 1.0 to 2.5
0.6 to 1.0
Molybdenum (Mo), % 2.5 to 3.5
0.3 to 0.5
Nickel (Ni), % 19 to 21
1.6 to 2.1
Niobium (Nb), % 0.75 to 1.3
0
Phosphorus (P), % 0 to 0.040
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.6
Sulfur (S), % 0 to 0.030
0 to 0.015
Tungsten (W), % 2.0 to 3.0
0