AWS E3155 vs. Grade Ti-Pd18 Titanium
AWS E3155 belongs to the iron alloys classification, while grade Ti-Pd18 titanium belongs to the titanium alloys. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is AWS E3155 and the bottom bar is grade Ti-Pd18 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 110 |
| Elongation at Break, % | 23 | |
| 17 |
| Poisson's Ratio | 0.29 | |
| 0.32 |
| Shear Modulus, GPa | 81 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 410 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1640 |
| Melting Onset (Solidus), °C | 1410 | |
| 1590 |
| Specific Heat Capacity, J/kg-K | 450 | |
| 550 |
| Thermal Conductivity, W/m-K | 13 | |
| 8.2 |
| Thermal Expansion, µm/m-K | 13 | |
| 9.1 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.4 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 7.7 | |
| 41 |
| Embodied Energy, MJ/kg | 110 | |
| 670 |
| Embodied Water, L/kg | 300 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 35 |
| Strength to Weight: Axial, points | 26 | |
| 44 |
| Strength to Weight: Bending, points | 22 | |
| 39 |
| Thermal Diffusivity, mm2/s | 3.3 | |
| 3.3 |
| Thermal Shock Resistance, points | 20 | |
| 52 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 2.5 to 3.5 |
| Carbon (C), % | 0 to 0.1 | |
| 0 to 0.1 |
| Chromium (Cr), % | 20 to 22.5 | |
| 0 |
| Cobalt (Co), % | 18.5 to 21 | |
| 0 |
| Copper (Cu), % | 0 to 0.75 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 23.3 to 36.3 | |
| 0 to 0.25 |
| Manganese (Mn), % | 1.0 to 2.5 | |
| 0 |
| Molybdenum (Mo), % | 2.5 to 3.5 | |
| 0 |
| Nickel (Ni), % | 19 to 21 | |
| 0 to 0.050 |
| Niobium (Nb), % | 0.75 to 1.3 | |
| 0 |
| Oxygen (O), % | 0 | |
| 0 to 0.15 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 92.5 to 95.5 |
| Tungsten (W), % | 2.0 to 3.0 | |
| 0 |
| Vanadium (V), % | 0 | |
| 2.0 to 3.0 |
| Residuals, % | 0 | |
| 0 to 0.4 |