AWS E316H vs. EN 1.7034 Steel

Both AWS E316H and EN 1.7034 steel are iron alloys. They have 66% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS E316H and the bottom bar is EN 1.7034 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 580
510 to 1780

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
45
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 20
2.2
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.0
1.4
Embodied Energy, MJ/kg 55
19
Embodied Water, L/kg 160
50

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
18 to 63
Strength to Weight: Bending, points 20
18 to 42
Thermal Diffusivity, mm2/s 4.0
12
Thermal Shock Resistance, points 15
15 to 52

Alloy Composition

Carbon (C), % 0.040 to 0.080
0.34 to 0.41
Chromium (Cr), % 17 to 20
0.9 to 1.2
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 58.6 to 69.5
97 to 98.2
Manganese (Mn), % 0.5 to 2.5
0.6 to 0.9
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 11 to 14
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.035