AWS E316H vs. SAE-AISI 94B17 Steel

Both AWS E316H and SAE-AISI 94B17 steel are iron alloys. They have 66% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is AWS E316H and the bottom bar is SAE-AISI 94B17 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
25
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Tensile Strength: Ultimate (UTS), MPa 580
440

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
39
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 20
2.4
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.0
1.5
Embodied Energy, MJ/kg 55
20
Embodied Water, L/kg 160
49

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
16
Strength to Weight: Bending, points 20
16
Thermal Diffusivity, mm2/s 4.0
10
Thermal Shock Resistance, points 15
13

Alloy Composition

Boron (B), % 0
0.00050 to 0.0030
Carbon (C), % 0.040 to 0.080
0.15 to 0.2
Chromium (Cr), % 17 to 20
0.3 to 0.5
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 58.6 to 69.5
97.1 to 98.3
Manganese (Mn), % 0.5 to 2.5
0.75 to 1.0
Molybdenum (Mo), % 2.0 to 3.0
0.080 to 0.15
Nickel (Ni), % 11 to 14
0.3 to 0.6
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.040