AWS E316H vs. N10624 Nickel
AWS E316H belongs to the iron alloys classification, while N10624 nickel belongs to the nickel alloys. They have a modest 30% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is AWS E316H and the bottom bar is N10624 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 220 |
| Elongation at Break, % | 34 | |
| 45 |
| Poisson's Ratio | 0.28 | |
| 0.3 |
| Shear Modulus, GPa | 78 | |
| 84 |
| Tensile Strength: Ultimate (UTS), MPa | 580 | |
| 810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 320 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1580 |
| Melting Onset (Solidus), °C | 1390 | |
| 1520 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 410 |
| Thermal Expansion, µm/m-K | 14 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 20 | |
| 70 |
| Density, g/cm3 | 7.9 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 4.0 | |
| 13 |
| Embodied Energy, MJ/kg | 55 | |
| 170 |
| Embodied Water, L/kg | 160 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 22 |
| Strength to Weight: Axial, points | 21 | |
| 25 |
| Strength to Weight: Bending, points | 20 | |
| 22 |
| Thermal Shock Resistance, points | 15 | |
| 24 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.5 |
| Carbon (C), % | 0.040 to 0.080 | |
| 0 to 0.010 |
| Chromium (Cr), % | 17 to 20 | |
| 6.0 to 10 |
| Cobalt (Co), % | 0 | |
| 0 to 1.0 |
| Copper (Cu), % | 0 to 0.75 | |
| 0 to 0.5 |
| Iron (Fe), % | 58.6 to 69.5 | |
| 5.0 to 8.0 |
| Manganese (Mn), % | 0.5 to 2.5 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 21 to 25 |
| Nickel (Ni), % | 11 to 14 | |
| 53.9 to 68 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.1 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.010 |