AWS E316L vs. AWS ERNiCrCoMo-1

AWS E316L belongs to the iron alloys classification, while AWS ERNiCrCoMo-1 belongs to the nickel alloys. They have a modest 36% of their average alloy composition in common, which, by itself, doesn't mean much. There are 24 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is AWS E316L and the bottom bar is AWS ERNiCrCoMo-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 34
28
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
81
Tensile Strength: Ultimate (UTS), MPa 550
710

Thermal Properties

Latent Heat of Fusion, J/g 290
330
Melting Completion (Liquidus), °C 1440
1420
Melting Onset (Solidus), °C 1390
1370
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 15
13
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 20
75
Density, g/cm3 7.9
8.5
Embodied Carbon, kg CO2/kg material 4.0
10
Embodied Energy, MJ/kg 55
140
Embodied Water, L/kg 160
350

Common Calculations

Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 19
23
Strength to Weight: Bending, points 19
21
Thermal Diffusivity, mm2/s 4.0
3.5
Thermal Shock Resistance, points 14
19

Alloy Composition

Aluminum (Al), % 0
0.8 to 1.5
Carbon (C), % 0 to 0.040
0.050 to 0.15
Chromium (Cr), % 17 to 20
20 to 24
Cobalt (Co), % 0
10 to 15
Copper (Cu), % 0 to 0.75
0 to 0.5
Iron (Fe), % 58.6 to 69.5
0 to 3.0
Manganese (Mn), % 0.5 to 2.5
0 to 1.0
Molybdenum (Mo), % 2.0 to 3.0
8.0 to 10
Nickel (Ni), % 11 to 14
42.7 to 61.2
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0 to 0.6
Residuals, % 0
0 to 0.5