AWS E316L vs. S24000 Stainless Steel

Both AWS E316L and S24000 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.

For each property being compared, the top bar is AWS E316L and the bottom bar is S24000 stainless steel.

AWS E316L (W31613) Weld Metal UNS S24000 (XM-29) Stainless Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		200

Elongation at Break, %		34
Elongation at Break, %		39

Poisson's Ratio		0.28
Poisson's Ratio		0.28

Shear Modulus, GPa		78
Shear Modulus, GPa		77

Tensile Strength: Ultimate (UTS), MPa		550
Tensile Strength: Ultimate (UTS), MPa		770

Thermal Properties

Latent Heat of Fusion, J/g		290
Latent Heat of Fusion, J/g		280

Melting Completion (Liquidus), °C		1440
Melting Completion (Liquidus), °C		1390

Melting Onset (Solidus), °C		1390
Melting Onset (Solidus), °C		1350

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		480

Thermal Expansion, µm/m-K		14
Thermal Expansion, µm/m-K		17

Otherwise Unclassified Properties

Base Metal Price, % relative		20
Base Metal Price, % relative		12

Density, g/cm³		7.9
Density, g/cm³		7.6

Embodied Carbon, kg CO₂/kg material		4.0
Embodied Carbon, kg CO₂/kg material		2.7

Embodied Energy, MJ/kg		55
Embodied Energy, MJ/kg		39

Embodied Water, L/kg		160
Embodied Water, L/kg		150

Common Calculations

PREN (Pitting Resistance)		27
PREN (Pitting Resistance)		23

Stiffness to Weight: Axial, points		14
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		25
Stiffness to Weight: Bending, points		25

Strength to Weight: Axial, points		19
Strength to Weight: Axial, points		28

Strength to Weight: Bending, points		19
Strength to Weight: Bending, points		24

Thermal Shock Resistance, points		14
Thermal Shock Resistance, points		16

Alloy Composition

Carbon (C), %		0 to 0.040
Carbon (C), %		0 to 0.080

Chromium (Cr), %		17 to 20
Chromium (Cr), %		17 to 19

Copper (Cu), %		0 to 0.75
Copper (Cu), %		0

Iron (Fe), %		58.6 to 69.5
Iron (Fe), %		61.5 to 69

Manganese (Mn), %		0.5 to 2.5
Manganese (Mn), %		11.5 to 14.5

Molybdenum (Mo), %		2.0 to 3.0
Molybdenum (Mo), %		0

Nickel (Ni), %		11 to 14
Nickel (Ni), %		2.3 to 3.7

Nitrogen (N), %		0
Nitrogen (N), %		0.2 to 0.4

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.060

Silicon (Si), %		0 to 1.0
Silicon (Si), %		0 to 0.75

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030