AWS E316LMn vs. EN 1.4513 Stainless Steel

Both AWS E316LMn and EN 1.4513 stainless steel are iron alloys. They have 73% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is AWS E316LMn and the bottom bar is EN 1.4513 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 23
26
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
77
Tensile Strength: Ultimate (UTS), MPa 620
480

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 14
10

Otherwise Unclassified Properties

Base Metal Price, % relative 24
10
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.6
2.5
Embodied Energy, MJ/kg 64
35
Embodied Water, L/kg 180
120

Common Calculations

PREN (Pitting Resistance) 32
21
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
17
Strength to Weight: Bending, points 20
18
Thermal Shock Resistance, points 15
17

Alloy Composition

Carbon (C), % 0 to 0.040
0 to 0.025
Chromium (Cr), % 18 to 21
16 to 18
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 47.5 to 59.4
77.7 to 83.1
Manganese (Mn), % 5.0 to 8.0
0 to 1.0
Molybdenum (Mo), % 2.5 to 3.5
0.8 to 1.4
Nickel (Ni), % 15 to 18
0
Nitrogen (N), % 0.1 to 0.25
0 to 0.020
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 0.9
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
0.15 to 0.8