AWS E316LMn vs. Grade Ti-Pd7B Titanium

AWS E316LMn belongs to the iron alloys classification, while grade Ti-Pd7B titanium belongs to the titanium alloys. There are 19 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.

For each property being compared, the top bar is AWS E316LMn and the bottom bar is grade Ti-Pd7B titanium.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 23
17
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 79
40
Tensile Strength: Ultimate (UTS), MPa 620
390

Thermal Properties

Latent Heat of Fusion, J/g 300
420
Melting Completion (Liquidus), °C 1420
1660
Melting Onset (Solidus), °C 1370
1610
Specific Heat Capacity, J/kg-K 470
540
Thermal Expansion, µm/m-K 14
8.7

Otherwise Unclassified Properties

Density, g/cm3 7.9
4.5
Embodied Carbon, kg CO2/kg material 4.6
49
Embodied Energy, MJ/kg 64
840
Embodied Water, L/kg 180
520

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
35
Strength to Weight: Axial, points 22
24
Strength to Weight: Bending, points 20
26
Thermal Shock Resistance, points 15
30

Alloy Composition

Carbon (C), % 0 to 0.040
0 to 0.1
Chromium (Cr), % 18 to 21
0
Copper (Cu), % 0 to 0.75
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 47.5 to 59.4
0 to 0.2
Manganese (Mn), % 5.0 to 8.0
0
Molybdenum (Mo), % 2.5 to 3.5
0
Nickel (Ni), % 15 to 18
0 to 0.050
Nitrogen (N), % 0.1 to 0.25
0
Oxygen (O), % 0
0 to 0.4
Palladium (Pd), % 0
0.12 to 0.3
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 0.9
0
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
98.8 to 99.9
Residuals, % 0
0 to 0.4