AWS E316LMn vs. ZA-27
AWS E316LMn belongs to the iron alloys classification, while ZA-27 belongs to the zinc alloys. There are 20 material properties with values for both materials. Properties with values for just one material (17, in this case) are not shown.
For each property being compared, the top bar is AWS E316LMn and the bottom bar is ZA-27.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 78 |
| Elongation at Break, % | 23 | |
| 2.0 to 4.5 |
| Poisson's Ratio | 0.28 | |
| 0.27 |
| Shear Modulus, GPa | 79 | |
| 31 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 400 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 130 |
| Melting Completion (Liquidus), °C | 1420 | |
| 480 |
| Melting Onset (Solidus), °C | 1370 | |
| 380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 530 |
| Thermal Expansion, µm/m-K | 14 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 24 | |
| 11 |
| Density, g/cm3 | 7.9 | |
| 5.0 |
| Embodied Carbon, kg CO2/kg material | 4.6 | |
| 4.2 |
| Embodied Energy, MJ/kg | 64 | |
| 80 |
| Embodied Water, L/kg | 180 | |
| 570 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 8.6 |
| Stiffness to Weight: Bending, points | 25 | |
| 28 |
| Strength to Weight: Axial, points | 22 | |
| 22 to 24 |
| Strength to Weight: Bending, points | 20 | |
| 24 to 25 |
| Thermal Shock Resistance, points | 15 | |
| 14 to 15 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 25 to 28 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0060 |
| Carbon (C), % | 0 to 0.040 | |
| 0 |
| Chromium (Cr), % | 18 to 21 | |
| 0 |
| Copper (Cu), % | 0 to 0.75 | |
| 2.0 to 2.5 |
| Iron (Fe), % | 47.5 to 59.4 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 0 to 0.0060 |
| Magnesium (Mg), % | 0 | |
| 0.010 to 0.020 |
| Manganese (Mn), % | 5.0 to 8.0 | |
| 0 |
| Molybdenum (Mo), % | 2.5 to 3.5 | |
| 0 |
| Nickel (Ni), % | 15 to 18 | |
| 0 to 0.020 |
| Nitrogen (N), % | 0.1 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 0.9 | |
| 0 to 0.080 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Zinc (Zn), % | 0 | |
| 69.3 to 73 |