AWS E317 vs. EN 1.4002 Stainless Steel

Both AWS E317 and EN 1.4002 stainless steel are iron alloys. They have 76% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS E317 and the bottom bar is EN 1.4002 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
19
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
76
Tensile Strength: Ultimate (UTS), MPa 620
500

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
30
Thermal Expansion, µm/m-K 14
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 22
7.0
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.3
1.9
Embodied Energy, MJ/kg 59
27
Embodied Water, L/kg 170
100

Common Calculations

PREN (Pitting Resistance) 31
13
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
18
Strength to Weight: Bending, points 20
18
Thermal Diffusivity, mm2/s 3.9
8.1
Thermal Shock Resistance, points 16
18

Alloy Composition

Aluminum (Al), % 0
0.1 to 0.3
Carbon (C), % 0 to 0.080
0 to 0.080
Chromium (Cr), % 18 to 21
12 to 14
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 56.6 to 66.5
83.6 to 87.9
Manganese (Mn), % 0.5 to 2.5
0 to 1.0
Molybdenum (Mo), % 3.0 to 4.0
0
Nickel (Ni), % 12 to 14
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.015