MakeItFrom.com
Menu (ESC)

AWS E317 vs. CC764S Brass

AWS E317 belongs to the iron alloys classification, while CC764S brass belongs to the copper alloys. There are 24 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS E317 and the bottom bar is CC764S brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 34
15
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 79
41
Tensile Strength: Ultimate (UTS), MPa 620
680

Thermal Properties

Latent Heat of Fusion, J/g 300
180
Melting Completion (Liquidus), °C 1450
850
Melting Onset (Solidus), °C 1400
810
Specific Heat Capacity, J/kg-K 470
400
Thermal Conductivity, W/m-K 15
94
Thermal Expansion, µm/m-K 14
20

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
32
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
36

Otherwise Unclassified Properties

Base Metal Price, % relative 22
23
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.3
2.9
Embodied Energy, MJ/kg 59
49
Embodied Water, L/kg 170
330

Common Calculations

Stiffness to Weight: Axial, points 14
7.6
Stiffness to Weight: Bending, points 25
20
Strength to Weight: Axial, points 22
24
Strength to Weight: Bending, points 20
22
Thermal Diffusivity, mm2/s 3.9
30
Thermal Shock Resistance, points 16
22

Alloy Composition

Aluminum (Al), % 0
1.0 to 3.0
Antimony (Sb), % 0
0 to 0.050
Carbon (C), % 0 to 0.080
0
Chromium (Cr), % 18 to 21
0
Copper (Cu), % 0 to 0.75
52 to 66
Iron (Fe), % 56.6 to 66.5
0.5 to 2.5
Lead (Pb), % 0
0 to 0.3
Manganese (Mn), % 0.5 to 2.5
0.3 to 4.0
Molybdenum (Mo), % 3.0 to 4.0
0
Nickel (Ni), % 12 to 14
0 to 3.0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
0 to 0.1
Sulfur (S), % 0 to 0.030
0
Tin (Sn), % 0
0 to 0.3
Zinc (Zn), % 0
20.7 to 50.2