AWS E317 vs. SAE-AISI 1023 Steel

Both AWS E317 and SAE-AISI 1023 steel are iron alloys. They have 62% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is AWS E317 and the bottom bar is SAE-AISI 1023 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
17 to 29
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 620
430 to 480

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
53
Thermal Expansion, µm/m-K 14
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 22
1.8
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.3
1.4
Embodied Energy, MJ/kg 59
18
Embodied Water, L/kg 170
45

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
15 to 17
Strength to Weight: Bending, points 20
16 to 17
Thermal Diffusivity, mm2/s 3.9
14
Thermal Shock Resistance, points 16
14 to 15

Alloy Composition

Carbon (C), % 0 to 0.080
0.2 to 0.25
Chromium (Cr), % 18 to 21
0
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 56.6 to 66.5
99.06 to 99.5
Manganese (Mn), % 0.5 to 2.5
0.3 to 0.6
Molybdenum (Mo), % 3.0 to 4.0
0
Nickel (Ni), % 12 to 14
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.030
0 to 0.050