AWS E317L vs. Grade FDSiCrV Steel

Both AWS E317L and grade FDSiCrV steel are iron alloys. They have 64% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS E317L and the bottom bar is grade FDSiCrV steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
80
Tensile Strength: Ultimate (UTS), MPa 580
2100

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Melting Completion (Liquidus), °C 1450
1440
Melting Onset (Solidus), °C 1400
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
47
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 22
2.3
Density, g/cm3 7.9
7.7
Embodied Carbon, kg CO2/kg material 4.3
1.9
Embodied Energy, MJ/kg 59
26
Embodied Water, L/kg 170
50

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 20
75
Strength to Weight: Bending, points 20
47
Thermal Diffusivity, mm2/s 3.9
13
Thermal Shock Resistance, points 15
63

Alloy Composition

Carbon (C), % 0 to 0.040
0.5 to 0.7
Chromium (Cr), % 18 to 21
0.5 to 1.0
Copper (Cu), % 0 to 0.75
0 to 0.12
Iron (Fe), % 56.6 to 66.5
96 to 97.8
Manganese (Mn), % 0.5 to 2.5
0.4 to 0.9
Molybdenum (Mo), % 3.0 to 4.0
0
Nickel (Ni), % 12 to 14
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 1.0
1.2 to 1.7
Sulfur (S), % 0 to 0.030
0 to 0.025
Vanadium (V), % 0
0.1 to 0.25