AWS E320 vs. EN 1.4477 Stainless Steel
Both AWS E320 and EN 1.4477 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is AWS E320 and the bottom bar is EN 1.4477 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Elongation at Break, % | 34 | |
| 22 to 23 |
| Poisson's Ratio | 0.28 | |
| 0.27 |
| Shear Modulus, GPa | 77 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 880 to 930 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 300 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1430 |
| Melting Onset (Solidus), °C | 1360 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 480 |
| Thermal Expansion, µm/m-K | 14 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 38 | |
| 20 |
| Density, g/cm3 | 8.2 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 6.5 | |
| 3.7 |
| Embodied Energy, MJ/kg | 91 | |
| 52 |
| Embodied Water, L/kg | 220 | |
| 190 |
Common Calculations
| PREN (Pitting Resistance) | 28 | |
| 41 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 21 | |
| 31 to 33 |
| Strength to Weight: Bending, points | 20 | |
| 26 to 27 |
| Thermal Shock Resistance, points | 16 | |
| 23 to 25 |
Alloy Composition
| Carbon (C), % | 0 to 0.070 | |
| 0 to 0.030 |
| Chromium (Cr), % | 19 to 21 | |
| 28 to 30 |
| Copper (Cu), % | 3.0 to 4.0 | |
| 0 to 0.8 |
| Iron (Fe), % | 31.8 to 43.5 | |
| 56.6 to 63.6 |
| Manganese (Mn), % | 0.5 to 2.5 | |
| 0.8 to 1.5 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 1.5 to 2.6 |
| Nickel (Ni), % | 32 to 36 | |
| 5.8 to 7.5 |
| Niobium (Nb), % | 0 to 1.0 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0.3 to 0.4 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.6 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.015 |