AWS E320 vs. SAE-AISI P4 Steel

Both AWS E320 and SAE-AISI P4 steel are iron alloys. They have 44% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS E320 and the bottom bar is SAE-AISI P4 steel.

AWS E320 (W88021) Weld Metal SAE-AISI P4 (T51604) Low-Carbon Mould Steel

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		200
Elastic (Young's, Tensile) Modulus, GPa		190

Poisson's Ratio		0.28
Poisson's Ratio		0.29

Shear Modulus, GPa		77
Shear Modulus, GPa		74

Tensile Strength: Ultimate (UTS), MPa		620
Tensile Strength: Ultimate (UTS), MPa		390 to 1980

Thermal Properties

Latent Heat of Fusion, J/g		300
Latent Heat of Fusion, J/g		260

Melting Completion (Liquidus), °C		1410
Melting Completion (Liquidus), °C		1460

Melting Onset (Solidus), °C		1360
Melting Onset (Solidus), °C		1420

Specific Heat Capacity, J/kg-K		460
Specific Heat Capacity, J/kg-K		470

Thermal Expansion, µm/m-K		14
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		38
Base Metal Price, % relative		4.4

Density, g/cm³		8.2
Density, g/cm³		7.8

Embodied Carbon, kg CO₂/kg material		6.5
Embodied Carbon, kg CO₂/kg material		1.8

Embodied Energy, MJ/kg		91
Embodied Energy, MJ/kg		23

Embodied Water, L/kg		220
Embodied Water, L/kg		68

Common Calculations

PREN (Pitting Resistance)		28
PREN (Pitting Resistance)		7.0

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		14

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		24

Strength to Weight: Axial, points		21
Strength to Weight: Axial, points		14 to 70

Strength to Weight: Bending, points		20
Strength to Weight: Bending, points		15 to 45

Thermal Shock Resistance, points		16
Thermal Shock Resistance, points		13 to 64

Alloy Composition

Carbon (C), %		0 to 0.070
Carbon (C), %		0 to 0.12

Chromium (Cr), %		19 to 21
Chromium (Cr), %		4.0 to 5.3

Copper (Cu), %		3.0 to 4.0
Copper (Cu), %		0 to 0.25

Iron (Fe), %		31.8 to 43.5
Iron (Fe), %		92.3 to 95.3

Manganese (Mn), %		0.5 to 2.5
Manganese (Mn), %		0.2 to 0.6

Molybdenum (Mo), %		2.0 to 3.0
Molybdenum (Mo), %		0.4 to 1.0

Nickel (Ni), %		32 to 36
Nickel (Ni), %		0

Niobium (Nb), %		0 to 1.0
Niobium (Nb), %		0

Phosphorus (P), %		0 to 0.040
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0 to 0.6
Silicon (Si), %		0.1 to 0.4

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.030