AWS E320LR vs. 364.0 Aluminum

AWS E320LR belongs to the iron alloys classification, while 364.0 aluminum belongs to the aluminum alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AWS E320LR and the bottom bar is 364.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
72
Elongation at Break, % 34
7.5
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 77
27
Tensile Strength: Ultimate (UTS), MPa 580
300

Thermal Properties

Latent Heat of Fusion, J/g 300
520
Melting Completion (Liquidus), °C 1410
600
Melting Onset (Solidus), °C 1360
560
Specific Heat Capacity, J/kg-K 460
900
Thermal Expansion, µm/m-K 14
21

Otherwise Unclassified Properties

Base Metal Price, % relative 36
11
Density, g/cm3 8.2
2.6
Embodied Carbon, kg CO2/kg material 6.2
8.0
Embodied Energy, MJ/kg 87
150
Embodied Water, L/kg 220
1080

Common Calculations

Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
53
Strength to Weight: Axial, points 20
31
Strength to Weight: Bending, points 19
38
Thermal Shock Resistance, points 15
14

Alloy Composition

Aluminum (Al), % 0
87.2 to 92
Beryllium (Be), % 0
0.020 to 0.040
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 19 to 21
0.25 to 0.5
Copper (Cu), % 3.0 to 4.0
0 to 0.2
Iron (Fe), % 32.7 to 42.5
0 to 1.5
Magnesium (Mg), % 0
0.2 to 0.4
Manganese (Mn), % 1.5 to 2.5
0 to 0.1
Molybdenum (Mo), % 2.0 to 3.0
0
Nickel (Ni), % 32 to 36
0 to 0.15
Niobium (Nb), % 0 to 0.4
0
Phosphorus (P), % 0 to 0.020
0
Silicon (Si), % 0 to 0.3
7.5 to 9.5
Sulfur (S), % 0 to 0.015
0
Tin (Sn), % 0
0 to 0.15
Zinc (Zn), % 0
0 to 0.15
Residuals, % 0
0 to 0.15